Beryllium Copper Rod/Bar

Wonder copper maintains an inventory of C17200 Beryllium Copper round rod and strip. Beryllium copper 17200 is a material with good corrosion resistance, rich in ductility before age hardening treatment, and increased in fatigue resistance and conductivity after age hardening treatment.

TYPICAL APPLICATIONS FOR BERYLLIUM COPPER ROD

  • Electrical Switch and Relay Blades
  • Electrical connectors
  • Non-Sparking Safety Tools
  • Pump Parts
  • Bushings/Bearing for
  • Aerospace Industry
  • Aircraft Engine Parts
  • Propellers
  • Bolts And Cams.
Wonder copper has been in the metal business since 1995 and our knowledgeable sales staff is able to help you with your Beryllium Copper needs. Contact us today. Wonder Copper is capable of producing the following grade of beryllium copper rod and bars, such as CuBe2-UNS.C17200 beryllium copper rods/ bars, CuBe2Pb-UNS.C17300 free cutting beryllium copper rods/bars, CuBe2Bi free lead, free cutting beryllium copper rod/bars (without Lead), CuCo2Be-UNS.C17500 Cobalt Beryllium Copper Rods/Bars, CuNi2Be-UNS.C17510 Nickel Beryllium Copper Rods/ Bars, CuCo1Ni1Be Cobalt Nickel Beryllium Copper Rods/Bars, CuNiBeTi Nickel Titanium Beryllium Copper Rod/bars, and the other bar forms: beryllium copper round bars, flat bars, square bars, rectangular bars, hexagonal bars are also available in Wonder Copper .

Production technology advantage

  • All products of the company are made of high-quality new materials, advanced production equipment, and vacuum melting furnaces. The metal materials are smelted under vacuum conditions, which can achieve the effect of high-temperature smelting and avoid oxidation of metal and oxygen in the air. Function, quality is more guaranteed;
  • 20MN double-action reverse extruder;
  • Equipped with comprehensive testing equipment such as universal testing machine, direct reading spectrometer, etc., to strictly control the quality and inspect layer by layer.

Chemical Composition

Executive standard:ASTM/GB/T5233-2001/EN12163(%max., unless shown as range or min.)
NumberingBeCo+NiCuFePbSiAl
C17200 1.8-2.0 Co+Ni≥0.2 Margin 0.15 - 0.15 0.15
C17300 1.8-2.0 Co+Ni≥0.2 Margin 0.15 0.2-0.6 0.15 0.15
C17500 0.4-0.7 Co 2.4-2.7 Margin 0.15 - 0.15 0.15
C17510 0.2-0.6 Co≤0.3,Ni 1.4-2.2 Margin 0.15 - 0.15 0.15
QBe2.0 1.8-2.1 Ni 0.2-0.5 Margin 0.15 0.005 0.15 0.15
BeCo1Ni1 0.4-0.7 Co 0.8-1.3,Ni 0.8-1.3 Margin 0.02 - 0.02 0.04

Mechanical properties and conductivity analysis

(AT/TF00)
Numbering Tensile Strength/MPa Yield Strength/MPa Elongation% Hardness Conductivity%IACS
C17200 1160-1380 980-1240 3-15 36-42HRC 22-28
C17300 1160-1380 980-1240 3-15 36-42HRC 22-28
C17500 700-920 560-710 10-25 92-100HRB 45-60
C17510 700-920 560-710 10-25 92-100HRB 45-60
QBe2.0 1160-1380 980-1240 3-15 36-42HRC 18-20
BeCo1Ni1 700-920 560-710 10-25 92-100HRB 45-60

Available Status

Brush Name ASTM Name Description
A TB00 Solution annealing state (quenched state)
½H TD01 Quarter hard
½H TD02 Half hard (semi-hard)
¾H TD03 Three-quarters hard
H TD04 Hard state (full hard)
AT TF00 Standard aging heat treatment in quenched state
¼HT TH01 Quarter hard standard aging heat treatment
½HT TH02 Half-hard standard aging heat treatment
¾HT TH03 Three-quarters hard standard aging heat treatment
HT TH04 Hard standard aging heat treatment (a process of comprehensive strengthening of deformation and aging)
Note: In the Brush name:
  • "A" represents the state of solution annealing (annealed, the alloy is in the softest state, easy to be stamped and formed, and needs to be cold worked or strengthened during the direct failure period);
  • "H" stands for cold processing state (hard);
  • "T" means that the material has been aging hardened by standard heat treatment (heat treatment means the state of aging strengthening heat treatment).